Alloyed hot-dip galvanized steel sheet and method of manufacturing the same

ABSTRACT

Provided is an alloyed hot-dip galvanized steel sheet including a base steel sheet, the base steel sheet containing a given amount of C, Si, Mn, and other elements. The alloyed hot-dip galvanized steel sheet is provided with an alloyed hot-dip galvanized layer on a surface of the base steel sheet, the alloyed hot-dip galvanized layer containing, in mass %, Fe: more than or equal to 5% and less than or equal to 15%, and having a thickness of more than or equal to 3 μm and less than or equal to 30 μm. The alloyed hot-dip galvanized steel sheet includes an A layer immediately under the surface of the base steel sheet, the A layer being formed in the base steel sheet and having a thickness of more than or equal to 2 μm and less than or equal to 20 μm from the surface of the base steel sheet, containing more than or equal to 50 vol % of a ferrite structure, and containing more than or equal to 90 mass % of unoxidized Fe, less than or equal to 10 mass % of a total of contents of oxides of Fe, Si, Mn, P, S, and Al, and less than 0.05 mass % of C.

This application is a Divisional of U.S. application Ser. No. 14/438,503, filed Apr. 24, 2015, which is the U.S. National Phase of PCT/JP2013/079858, filed Nov. 5, 2013, which claims priority under 35 U.S.C. 119(a) to Japanese Patent Application No. 2012-244274, filed Nov. 6, 2012, the contents of all of which are incorporated by reference, in their entirety, into the present application.

TECHNICAL FIELD

The present invention relates to an alloyed hot-dip galvanized steel sheet and a method of manufacturing the same. In more detail, present invention relates to a high-strength alloyed hot-dip galvanized steel sheet having a tensile strength of 590 MPa or more, including an alloyed hot-dip galvanized layer having excellent wettability of plating and adhesion of plated layer which can be applied as a material used in an automotive field, a household appliance field, and a building material field, and to a method of manufacturing the same.

BACKGROUND ART

In materials used in an automotive field, a household appliance field, and a building material field, a surface treated steel sheet which is imparted with corrosion prevention is being used. In particular, an alloyed hot-dip galvanized steel sheet which can be produced at low cost and is excellent in corrosion prevention is being used.

In general, the alloyed hot-dip galvanized steel sheet is manufactured by the following method using a continuous hot-dip galvanizing plant. First, a slab is hot rolled, cold rolled, or heat treated to obtain a thin-gauge steel sheet. The thin-gauge steel sheet is degreased and/or pickled in a pretreatment step for the purpose of cleaning the surface of the base steel sheet or, omitting the pretreatment step, is heated in a preheating furnace to burn off the oil on the surface of the base steel sheet, then is subjected to heating and recrystallization annealing. The atmosphere at the time of performing the recrystallization annealing is an Fe reducing atmosphere since at the time of the later plating treatment, Fe oxides would obstruct the wettability of the plated layer and the base steel sheet or the adhesion of the plated layer and the base steel sheet. After the recrystallization annealing, without contacting the air, the steel sheet is continuously cooled to a temperature suitable for plating in an Fe reducing atmosphere and dipped in a hot-dip galvanizing bath for hot-dip galvanization. After the hot-dip galvanization, the amount of adhesion of the plating is controlled by immediately performing wiping by nitrogen gas. After that, the heating is performed to thereby conduct an Fe—Zn alloying reaction, and in this way, the alloyed hot-dip galvanized layer is formed on the base steel sheet.

In recent years, in particular in the automotive field, to achieve both the function of protecting the passengers at the time of collision and lighter weight aimed at improvement of the fuel efficiency, use of a high-strength steel sheet which is made higher in strength of the base steel sheet by inclusion of elements which are relatively inexpensive, such as C, Si, and Mn, has been increasing. Regarding the strength, the steel sheet having a tensile strength of 590 MPa or more is mainly used.

However, in the high-strength alloyed hot-dip galvanized steel sheet including Si and Mn, Si and Mn are elements which are more easily oxidizable compared with Fe, so at the time of heating in recrystallization annealing in a conventional Fe-reducing atmosphere, Si and Mn on the surface of the steel sheet oxidize. Further, Si and Mn which thermally diffuse from the inside of the steel sheet oxidize at the steel sheet surface whereby gradually the Si and Mn oxides become concentrated on the surface. If the Si and Mn oxides concentrate at the surface, in the process of dipping the steel sheet in the hot-dip galvanizing bath, contact between the molten zinc and the base steel sheet would be prevented, which would cause a drop in the wettability of plating and the adhesion of plated layer of the alloyed hot-dip galvanized layer. If the plating layer deteriorates in wettability, nonplating defects occur and result in defects in appearance and defects in corrosion prevention. If the adhesion of plated layer deteriorates, peeling of the plating occurs when press forming is performed, and results in problems including defects in corrosion prevention and defects in appearance with press scratches and the like.

Further, in the high-strength alloyed hot-dip galvanized steel sheet containing C, when C is present in a grain boundary or a grain of the base steel sheet in the recrystallization annealing, there is a problem in that the reaction between the molten zinc and the steel sheet in the process of Fe—Zn alloying reaction after dipping the base steel sheet in the hot-dip galvanizing bath is inhibited, to thereby deteriorate the adhesion of plated layer. In addition, there is also a problem in that the inclusion of C in the alloyed hot-dip galvanized layer after the alloying reaction lowers the ductility of the plating, so that peeling of the plating easily occurs when press forming is performed.

Still further, in the high-strength alloyed hot-dip galvanized steel sheet, the ductility deteriorates with the increase in the strength of the base steel sheet, and along therewith, pressing load at the time of performing press forming is large, so that the shear stress applied to the plated layer from a mold at the time of performing forming increases. Accordingly, there is a problem that the plated layer is easily peeled from the interface with the base steel sheet, and results in problems including defects in corrosion prevention and defects in appearance with press scratches and the like.

As measures for the problems attributed to the concentration of oxides of Si and Mn at the time of annealing, there have been proposed various techniques in the past.

As the technique focusing on suppressing concentration of oxides of Si and Mn, Patent Literature 1 shows a method including performing annealing under an oxidizing atmosphere of Si so that the thickness of the oxide film of the steel sheet surface becomes 400 to 10000 Å, then reducing the Fe in the furnace atmosphere containing hydrogen, and performing plating. Further, Patent Literature 2 shows a method including oxidizing the Fe on the steel sheet surface, controlling the oxygen potential in the reducing furnace to thereby reduce the Fe and internally oxidize the Si so as to suppress the concentration of Si oxides on the surface, and then performing plating. However, in those techniques, if the reduction time is too long, Si concentrates at the surface, and if the reduction time is too short, an Fe oxide film remains on the steel sheet surface. Accordingly, there is the problem that issues in the plating layer wettability and the plating layer adhesion are insufficiently resolved. In addition, if Fe oxides are formed on the steel sheet surface inside an annealing furnace, the Fe oxides are deposited on a roll inside the furnace, and with increase in the amount of the deposit, there is a problem that roll pickup is caused, such as defects in appearance with press scratches on the steel sheet.

Patent Literature 3 shows a technique of suppressing the concentration of oxides of Si and Mn on the surface by raising the oxygen potential in the atmosphere in an all radiant tube type annealing furnace and internally oxidizing Si and Mn. Further, Patent Literatures 4 and 5 show methods including carefully controlling the means and conditions for raising the oxygen potential to suppress the surface concentration of both Fe oxides and Si and Mn oxides, and then performing plating. However, none of those techniques are insufficient in suppressing the concentration of oxides of Si and Mn. Further, since internal oxides of Si and Mn formed on the surface of the base steel sheet are present in the vicinity of the surface of the inside of the base steel sheet, there is a problem that the ductility of the base steel sheet deteriorates and the press forming cannot be performed. In addition, when a shear stress is applied to the plated layer at the time of performing the press forming, there is a problem that the plated layer peels from the vicinity of the surface of the inside of the base steel sheet in which the internal oxides are present.

Patent Literature 6 shows a method including raising the hydrogen concentration in the atmosphere in the recrystallization annealing up to the reducing region in which Fe, Si, and Mn do not oxidize, and performing plating. However, in this technique, there is a problem in addition to that the cost of hydrogen becomes immense, that the presence of C on the surface of the base steel sheet deteriorates the adhesion of plated layer as described above, and the remaining Si and Mn obstruct the reaction between the plating and the base steel sheet and form oxides of Si and Mn by being reacted with oxides floating on the surface of the bath at the time of dipping in the plating bath, so the wettability of plating and the adhesion of plated layer deteriorate.

Further, as a technique for suppressing the concentration of oxides of Si and Mn, Patent Literature 7, which focuses on causing internal oxidation in advance in the hot rolling step, shows a technique of controlling the oxygen potential in the hot rolling step so as to cause internal oxidation of Si and using the resultant thin-gauge steel sheet to manufacture a hot-dip galvanized steel sheet in a continuous hot-dip galvanizing plant. However, in this technique, at the time of the cold rolling step and other rolling, the layer of internal oxidation also ends up being rolled together, so the internal oxidation layer becomes smaller in thickness and Si oxides end up concentrating on the surface in the recrystallization annealing process, so there is a problem that the wettability of plating and the adhesion of plated layer are insufficiently improved. Further, there is a problem that oxides of Fe, which are formed simultaneously with internal oxidization of Si in the hot rolling step, cause roll pickup.

Further, the techniques written in Patent Literatures 1 to 7 are insufficient for solving the problem of the adhesion of plated layer related to the deterioration of ductility caused by increase in the strength of the alloyed hot-dip galvanized steel sheet.

PRIOR ART LITERATURE(S) Patent Literature(s)

-   [Patent Literature 1] JP 555-122865A -   [Patent Literature 2] JP 2001-323355A -   [Patent Literature 3] JP 2008-7842A -   [Patent Literature 4] JP 2001-279412A -   [Patent Literature 5] JP 2009-209397A -   [Patent Literature 6] JP 2010-126757A -   [Patent Literature 7] JP 2000-309847A

SUMMARY OF THE INVENTION Problem(s) to Be Solved by the Invention

The present invention provides a high-strength alloyed hot-dip galvanized steel sheet including an alloyed hot-dip galvanized layer having excellent wettability of plating and adhesion of plated layer on a base steel sheet containing C, Si, and Mn, and a method of manufacturing the same.

Means for Solving the Problem(s)

In order to solve the problems, the inventors of the present invention have focused on influences on the wettability of plating and the adhesion of plated layer of a content of a ferrite structure, a content of unoxidized Fe, contents of oxides of Fe, Si, and Mn, and a content of C in the steel sheet which is immediately under the base steel sheet in particular, among the alloyed hot-dip galvanized layer and the base steel sheet in the alloyed hot-dip galvanized steel sheet. Further, as the method of manufacturing the alloyed hot-dip galvanized steel sheet, the inventors of the present invention have focused on controlling, in a continuous hot-dip galvanizing plant including a heating furnace and a soaking furnace, a value of a logarithm log(P_(H2O)/P_(H2)) of a value obtained by dividing a partial water vapor pressure P_(H2O) by a partial hydrogen pressure (P_(H2)) of an atmosphere in each of the heating furnace and the soaking furnace, in each of the heating furnace and the soaking furnace, and have conducted intensive studies. As a result, the inventors of the present invention have found that a high-strength alloyed hot-dip galvanized steel sheet having excellent wettability of plating and adhesion of plated layer and having a tensile strength of 590 MPa or more can be manufactured, and thus, the present invention has been made.

That is, the gist of the present invention is as follows.

-   [1] An alloyed hot-dip galvanized steel sheet including a base steel     sheet,

wherein the base steel sheet contains, in mass %,

C: more than or equal to 0.05% and less than or equal to 0.50%,

Si: more than or equal to 0.2% and less than or equal to 3.0%,

Mn: more than or equal to 0.5% and less than or equal to 5.0%,

Al: more than or equal to 0.001 and less than or equal to 1.0%,

P: less than or equal to 0.1%,

S: less than or equal to 0.01%,

N: less than or equal to 0.01%, and

the balance including Fe and inevitable impurities,

wherein the alloyed hot-dip galvanized steel sheet is provided with an alloyed hot-dip galvanized layer on a surface of the base steel sheet, the alloyed hot-dip galvanized layer containing, in mass %, Fe: more than or equal to 5% and less than or equal to 15%, and the balance including Zn and inevitable impurities, and having a thickness of more than or equal to 3 μm and less than or equal to 30 μm, and wherein the alloyed hot-dip galvanized steel sheet includes an A layer immediately under the surface of the base steel sheet, the A layer being formed in the base steel sheet and having a thickness of more than or equal to 2 μm and less than or equal to 20 μm from the surface of the base steel sheet, the A layer containing more than or equal to 50 vol % of a ferrite structure based on a volume of the A layer and the balance including inevitable structures, and containing, based on a mass of the A layer, more than or equal to 90 mass % of unoxidized Fe, less than or equal to 10 mass % of a total of contents of oxides of Fe, Si, Mn, P, S, and Al, and less than 0.05 mass % of C.

-   [2] The alloyed hot-dip galvanized steel sheet according to [1],

wherein the base steel sheet further contains one or more of, in mass %,

Cr: more than or equal to 0.05% and less than or equal to 1.0%,

Ni: more than or equal to 0.05% and less than or equal to 1.0%,

Cu: more than or equal to 0.05% and less than or equal to 1.0%,

Nb: more than or equal to 0.005% and less than or equal to 0.3%,

Ti: more than or equal to 0.005% and less than or equal to 0.3%,

V: more than or equal to 0.005% and less than or equal to 0.5%,

B: more than or equal to 0.0001% and less than or equal to 0.01%,

Ca: more than or equal to 0.0005% and less than or equal to 0.04%,

Mg: more than or equal to 0.0005% and less than or equal to 0.04%,

La: more than or equal to 0.0005% and less than or equal to 0.04%,

Ce: more than or equal to 0.0005% and less than or equal to 0.04%, and

Y: more than or equal to 0.0005% and less than or equal to 0.04%.

-   [3] The alloyed hot-dip galvanized steel sheet according to [1] or     [2], wherein the alloyed hot-dip galvanized layer further contains,     in mass %, Al: more than or equal to 0.02% and less than or equal to     1.0%. -   [4] A method of manufacturing an alloyed hot-dip galvanized steel     sheet including a base steel material, the base steel material     containing, in mass %,

C: more than or equal to 0.05% and less than or equal to 0.50%,

Si: more than or equal to 0.2% and less than or equal to 3.0%,

Mn: more than or equal to 0.5% and less than or equal to 5.0%,

Al: more than or equal to 0.001 and less than or equal to 1.0%,

P: less than or equal to 0.1%,

S: less than or equal to 0.01%,

N: less than or equal to 0.01%, and

the balance including Fe and inevitable impurities,

the method including:

performing casting, hot-rolling, pickling, and cold rolling to thereby produce the base steel material;

subjecting the base steel material to a hot-dip galvanizing treatment by performing, using a continuous hot-dip galvanizing plant equipped with a heating furnace and a soaking furnace, an annealing treatment in which a temperature of the base steel material is increased within a range of higher than or equal to 500° C. and lower than or equal to 950° C. in the heating furnace and the soaking furnace; and

subjecting the base steel material to an alloying treatment at higher than or equal to 440° C. and lower than or equal to 600° C.,

wherein the annealing treatment is performed under the following conditions:

-   -   conditions of the heating furnace: an all radiant tube type         heating furnace is used, a time period that the temperature of         the base steel material is in the range of higher than or equal         to 500° C. and lower than or equal to 950° C. is 100 seconds to         1000 seconds, an atmosphere of the heating furnace contains         hydrogen, water vapor, and nitrogen, a logarithm         log(P_(H2O)/P_(H2)) of a value obtained by dividing a partial         water vapor pressure (P_(H2O)) by a partial hydrogen pressure         (P_(H2)) is more than or equal to −4.0 and less than −2.0, and a         hydrogen concentration is more than or equal to 3 vol % and less         than or equal to 30 vol %; and     -   conditions of the soaking furnace: a time period that the         temperature of the base steel material is in the range of higher         than or equal to 500° C. and lower than or equal to 950° C. is         100 seconds to 1000 seconds, an atmosphere of the soaking         furnace contains hydrogen, water vapor, and nitrogen, a         logarithm log(P_(H2O)/P_(H2)) of a value obtained by dividing a         partial water vapor pressure (P_(H2O)) by a partial hydrogen         pressure (P_(H2)) is more than or equal to −8.0 and less than         −4.0, and a hydrogen concentration is more than or equal to 3         vol % and less than or equal to 30 vol %.

-   [5] A method of manufacturing the alloyed hot-dip galvanized steel     sheet according to [4],

wherein the base steel material further contains one or more of, in mass %,

Cr: more than or equal to 0.05% and less than or equal to 1.0%,

Ni: more than or equal to 0.05% and less than or equal to 1.0%,

Cu: more than or equal to 0.05% and less than or equal to 1.0%,

Nb: more than or equal to 0.005% and less than or equal to 0.3%,

Ti: more than or equal to 0.005% and less than or equal to 0.3%,

V: more than or equal to 0.005% and less than or equal to 0.5%,

B: more than or equal to 0.0001% and less than or equal to 0.01%,

Ca: more than or equal to 0.0005% and less than or equal to 0.04%,

Mg: more than or equal to 0.0005% and less than or equal to 0.04%,

La: more than or equal to 0.0005% and less than or equal to 0.04%,

Ce: more than or equal to 0.0005% and less than or equal to 0.04%, and

Y: more than or equal to 0.0005% and less than or equal to 0.04%.

Effect(s) of the Invention

According to the present invention, there is provided the high-strength alloyed hot-dip galvanized steel sheet including the alloyed hot-dip galvanized layer having excellent wettability of plating and adhesion of plated layer on the base steel sheet containing C, Si, and Mn and having a tensile strength of 590 MPa or more.

BRIEF DESCRIPTION OF THE DRAWING(S)

FIG. 1 is a graph showing a relationship of an Fe content in an alloyed hot-dip galvanized layer and a thickness of the alloyed hot-dip galvanized layer to wettability of plating and adhesion of plated layer, which is obtained from results of Examples and Comparative Examples of the present invention to be described later.

FIG. 2 is a graph showing a relationship of a log(P_(H2O)/P_(H2)) of a heating furnace and a ferrite structure content in an A layer to wettability of plating and adhesion of plated layer, which is obtained from results of Examples and Comparative Examples of the present invention to be described later.

FIG. 3 is a graph showing a relationship of a log(P_(H2O)/P_(H2)) of a soaking furnace and a content of unoxidized Fe in an A layer to wettability of plating and adhesion of plated layer, which is obtained from results of Examples and Comparative Examples of the present invention to be described later.

FIG. 4 is a graph showing a relationship of a log(P_(H2O)/P_(H2)) of a soaking furnace and a total of contents of oxides of Fe, Si, Mn, P, S, and Al in an A layer to wettability of plating and adhesion of plated layer, which is obtained from results of Examples and Comparative Examples of the present invention to be described later.

FIG. 5 is a graph showing a relationship of a log(P_(H2O)/P_(H2)) of a heating furnace and a C content in an A layer to wettability of plating and adhesion of plated layer, which is obtained from results of Examples and Comparative Examples of the present invention to be described later.

FIG. 6 is a graph showing a relationship of a log(P_(H2O)/P_(H2)) of a heating furnace and a thickness of an A layer to wettability of plating and adhesion of plated layer, which is obtained from results of Examples and Comparative Examples of the present invention to be described later.

FIG. 7 is a graph showing a relationship of maximum sheet temperature of a heating furnace and a time period that temperature of a cold-rolled steel sheet is in a range of higher than or equal to 500° C. and lower than or equal to 950° C. in the heating furnace to wettability of plating and adhesion of plated layer, which is obtained from results of Examples and Comparative Examples of the present invention to be described later.

FIG. 8 is a graph showing a relationship of maximum sheet temperature of a soaking furnace and a time period that temperature of a cold-rolled steel sheet is in a range of higher than or equal to 500° C. and lower than or equal to 950° C. in the soaking furnace to wettability of plating and adhesion of plated layer, which is obtained from results of Examples and Comparative Examples of the present invention to be described later.

FIG. 9 is a graph showing a relationship of a log(P_(H2O)/P_(H2)) of a heating furnace and a log(P_(H2O)/P_(H2)) of a soaking furnace to wettability of plating and adhesion of plated layer, which is obtained from results of Examples and Comparative Examples of the present invention to be described later.

FIG. 10 is a graph showing a relationship of a hydrogen concentration in a heating furnace and a hydrogen concentration in a soaking furnace to wettability of plating and adhesion of plated layer, which is obtained from results of Examples and Comparative Examples of the present invention to be described later.

FIG. 11 is a graph showing a relationship of alloying temperature in an alloying treatment and an Fe content in an alloyed hot-dip galvanized layer to wettability of plating and adhesion of plated layer, which is obtained from results of Examples and Comparative Examples of the present invention to be described later.

MODE(S) FOR CARRYING OUT THE INVENTION

Hereinafter, the present invention will be described in detail.

First, let us assume that steel components of the base steel sheet including the alloyed hot-dip galvanized layer according to the present invention are as follows, and in addition, the base steel sheet has a tensile strength of 590 MPa or more. Note that “%” used for the steel components described in the following description represents “mass %” unless otherwise particularly explained.

C: C is an element which can increase the strength of the base steel sheet.

However, when the content is less than 0.05%, it is difficult to achieve both of the tensile strength of 590 MPa or more and the workability. On the other hand, when the content exceeds 0.50%, it is difficult to ensure the spot weldability. For this reason, the range is set to more than or equal to 0.05% and less than or equal to 0.50%.

Si: Si is a strengthening element and is effective for increasing the strength of the base steel sheet. Si can suppress precipitation of cementite. When the content is less than 0.2%, the effect of high strengthening is small. On the other hand, when the content exceeds 3.0%, the workability is decreased. Accordingly, the content of Si is set to the range of more than or equal to 0.2% and less than or equal to 3.0%.

Mn: Mn is a strengthening element and is effective for increasing the strength of the base steel sheet. However, when the content is less than 0.5%, it is difficult to obtain the tensile strength of 590 MPa or more. Conversely, when the content is a large quantity, it facilitates co-segregation with P and S and leads to a remarkable deterioration in the workability, and thus the upper limit is 5.0%. Accordingly, the content of Mn is set to the range of more than or equal to 0.5% and less than or equal to 5.0%.

Al: Al promotes the formation of ferrite, and improves the ductility. Al can also act as a deoxidizing material. The effects thereof are insufficient when the content is less than 0.001%. On the other hand, excessive addition increases the number of Al-based coarse inclusions, which can cause the deterioration in hole expandability as well as surface defects. Accordingly, the content of Al is set to more than or equal to 0.001% and less than or equal to 1.0%.

P: P tends to segregate at the center part of thickness of the steel sheet and causes the weld zone to become brittle. When the content exceeds 0.1%, the embrittlement of the weld zone becomes remarkable, so the suitable range is set to less than or equal to 0.1%. That is, P is regarded as an impurity and is limited to less than or equal to 0.1%. The lower limit value of P is not particularly determined, but when the lower limit is less than 0.0001%, it is disadvantageous economically, so this value is preferably set to the lower limit value.

S: S has an adverse effect on the weldability and on the manufacturability at the time of casting and hot rolling. For this reason, the upper limit value is less than or equal to 0.01%. That is, S is regarded as an impurity and is limited to less than or equal to 0.01%. The lower limit value of S is not particularly determined, but when the lower limit is less than 0.0001%, it is disadvantageous economically, so this value is preferably set to the lower limit value. Since S combines with Mn to form coarse MnS, which deteriorates the bendability and the hole expandability, it is preferred that the content of S be reduced as much as possible.

N: N forms coarse nitrides and causes the deterioration of the bendability and hole expandability, so it is necessary to restrict the additive amount. This is because when the content of N exceeds 0.01%, the above tendency becomes remarkable, so N is regarded as an impurity and the content of N is in a range of less than or equal to 0.01%. The effect of the present invention is exhibited without particularly limiting the lower limit, but when the content of N is less than 0.0005%, the manufacturing cost dramatically increases, so this value is a substantial lower limit.

The base steel sheet according to the present invention may further include, as necessary, one or more selected from the group consisting of Cr, Ni, Cu, Nb, Ti, V, B, Ca, Mg, La, Ce, and Y.

Cr: Cr is a strengthening element and is important for improvement of hardenability. However, when the content is less than 0.05%, these effects cannot be obtained, so, in the case of including Cr, the lower limit value is set to 0.05%. Conversely, when the content exceeds 1.0%, it has an adverse effect on the manufacturability at the time of manufacturing and hot rolling, so the upper limit value is set to 1.0%.

Ni: Ni is a strengthening element and is important for improvement of hardenability. However, when the content is less than 0.05%, these effects cannot be obtained, so, in the case of including Ni, the lower limit value is set to 0.05%. Conversely, when the content exceeds 1.0%, it has an adverse effect on the manufacturability at the time of manufacturing and hot rolling, so the upper limit value is set to 1.0%.

Cu: Cu is a strengthening element and is important for improvement of hardenability. However, when the content is less than 0.05%, these effects cannot be obtained, so, in the case of including Cu, the lower limit value is set to 0.05%. Conversely, when the content exceeds 1.0%, it has an adverse effect on the manufacturability at the time of manufacturing and hot rolling, so the upper limit value is set to 1.0%.

Nb: Nb is a strengthening element. It helps to increase the strength of the base steel sheet through the precipitate strengthening, the grain-refining strengthening due to the growth inhibition of ferrite crystal grains, and the dislocation strengthening due to the inhibition of recrystallization. When the additive amount is less than 0.005%, these effects cannot be obtained, so, in the case of including Nb, the lower limit value is set to 0.005%. When the content exceeds 0.3%, the carbonitride precipitation increases and the formability tends to deteriorate, so the upper limit is set to 0.3%.

Ti: Ti is a strengthening element. It helps to increase the strength of the base steel sheet through precipitate strengthening, grain-refining strengthening due to the growth inhibition of ferrite crystal grains, and dislocation strengthening due to the inhibition of recrystallization. When the additive amount is less than 0.005%, these effects cannot be obtained, so, in the case of including Ti, the lower limit value is set to 0.005%. When the content exceeds 0.3%, carbonitride precipitation increases and the formability tends to deteriorate, so the upper limit is set to 0.3%.

V: V is a strengthening element. It helps to increase the strength of the steel sheet through the precipitate strengthening, the grain-refining strengthening due to the growth inhibition of ferrite crystal grains, and the dislocation strengthening due to the inhibition of recrystallization. When the additive amount is less than 0.005%, these effects cannot be obtained, so, in the case of including V, the lower limit value is set to 0.005%. When the content exceeds 0.5%, the carbonitride precipitation increases and the formability tends to deteriorate, so the upper limit is set to 0.5%.

B: B is effective for grain boundary strengthening and steel strengthening by addition of more than or equal to 0.0001%, but when the additive amount thereof exceeds 0.01%, not only the effect of addition becomes saturated, but the manufacturability at the time of hot rolling is decreased, so the upper limit thereof is set to 0.01%.

Ca, Mg, La, Ce, and Y may each be included more than or equal to 0.0005% and less than or equal to 0.04%. Ca, Mg, La, Ce, and Y are elements used for deoxidation, and it is preferred that the content of each of the elements be more than or equal to 0.0005%. However, when the content exceeds 0.04%, this may cause deterioration of the formability. Accordingly, the content of each of the elements is set to more than or equal to 0.0005% and less than or equal to 0.04%.

Note that, in the present invention, La, Ce, and Y are generally added in a mischmetal, which in addition to La and Ce may also contain other lanthanoid series elements in combination. The effects of the present invention are exhibited even when the lanthanoid series elements other than La and Ce are contained as inevitable impurities. However, the effects of the present invention are exhibited even when metals such as La and Ce are added.

Next, the alloyed hot-dip galvanized layer according to the present invention will be described.

The alloyed hot-dip galvanized layer according to the present invention is formed on a surface of the base steel sheet, which is a substrate, for ensuring corrosion prevention. Accordingly, in the present invention, the lowering of the adhesion of plated layer or the wettability of plating is a disadvantageous problem from the viewpoint of ensuring the corrosion prevention.

As shown in FIG. 1, the alloyed hot-dip galvanized layer includes, in mass %, more than or equal to 5% and less than or equal to 15% of Fe, the balance including Zn and inevitable impurities.

When the Fe content is less than 5%, the amount of an Fe—Zn alloy phase formed in the plated layer is small and the corrosion prevention is insufficient. In addition, since slidability of the surface of the plated layer decreases, base steel sheet fracture or plated layer peeling occurs at the time of performing press forming, and hence, the adhesion of plated layer deteriorates. When the Fe content exceeds 15%, in the Fe—Zn alloy phase formed in the plated layer, a Γ phase or a Γ1 phase which is poor in ductility is formed with a large thickness. As a result thereof, at the interface between the plated layer and the substrate steel sheet, the plated layer peels at the time of performing press forming, and the corrosion prevention deteriorates. Note that the Fe—Zn alloy phase used here represents all of the following: a ζ phase (FeZn₁₃), a δ₁ phase (FeZn₇), a Γ₁ phase (Fe₅Zn₂₁), and a Γ phase (Fe₃Zn₁₀).

Further, in the present invention, Al may further be included in the plated layer as necessary. With inclusion of more than or equal to 0.02% and less than or equal to 1.0% of Al in the plated layer, the wettability of plating and the adhesion of plated layer can be further enhanced.

A method of analyzing the Fe content per plated layer involves for example: cutting an area of 30 mm×30 mm from the alloyed hot-dip galvanized steel sheet; immersing the cut sample in 5% aqueous solution of hydrochloric acid containing 0.02 vol % of inhibitor (IBIT 700A, manufactured by Asahi Chemical Co., Ltd); dissolving only the alloyed hot-dip galvanized layer; measuring the amount of Fe, the amount of Zn, and the amount of Al of the solution with ICP (ion plasma emission analyzer); and dividing the amount of Fe by the amount of Fe + the amount of Zn + the amount of Al and multiplying the result by 100. In the present invention, the Fe content represents an average of the values determined from five samples which are cut from locations that are spaced apart from each other by 100 mm or more.

As shown in FIG. 1, the alloyed hot-dip galvanized layer has a thickness of more than or equal to 3 μm and less than or equal to 30 μm.

The alloyed hot-dip galvanized layer having the thickness of less than 3 μm is insufficient in the corrosion prevention. In addition, it becomes difficult to uniformly form the plated layer on the base steel sheet, which may cause unplating, for example, and thus, the wettability of plating deteriorates. The alloyed hot-dip galvanized layer having the thickness exceeding 30 μm is not economical, because the effect of enhancing the corrosion prevention by the plated layer saturates. In addition, residual stress inside the plated layer increases, and the adhesion of plated layer deteriorates, for example, the plated layer may be peeled at the time of performing press forming.

Regarding a method of measuring the thickness of the alloyed hot-dip galvanized layer, there are various methods including the microscopic cross-section test method (JIS H 8501). This is a method of burying a cross-section of a sample in a resin, polishing it, then performing etching by a corrosive solution as necessary, and analyzing the polished surface by an optical microscope, a scan type electron microscope (SEM), an electron probe microanalyzer (EPMA), and the like, and finding the thickness. In the present invention, the sample was buried in Technovit 4002 (manufactured by Maruto Instrument Co., Ltd.) and polished in order by #240, #320, #400, #600, #800, and #1000 polishing paper (JIS R 6001), then the polished surface was analyzed by EPMA from the surface of the plated layer to the substrate steel sheet by line analysis. Then, the thickness at which Zn is no longer detected was found at positions of any 10 locations that are spaced apart from each other by 1 mm or more, the found values are averaged, and the obtained value was determined to be the thickness of the alloyed hot-dip galvanized layer.

Subsequently, an A layer, which is important in the present invention, will be described.

The alloyed hot-dip galvanized steel sheet according to the present invention includes the following A layer immediately under the surface of the base steel sheet, the A layer being formed in the base steel sheet and having a thickness of more than or equal to 2 μm and less than or equal to 20 μm from the surface of the base steel sheet.

A layer: including more than or equal to 50 vol % of a ferrite structure based on a volume of the A layer and the balance including inevitable structures, and containing, based on a mass of the A layer, more than or equal to 90 mass % of unoxidized Fe, less than or equal to 10 mass % of a total of contents of oxides of Fe, Si, Mn, P, S, and Al, and less than 0.05 mass % of C.

The A layer according to the present invention is defined by the following measurement method. Since the oxides of Fe, Si, Mn, P, S, and Al are decreased, the A layer is mainly composed of a ferrite structure suppressed in C and excellent in ductility, which is different from a layer including internal oxides of Si and Mn or externally oxidized Si and Mn written in Patent Literatures or the like. Further, the A layer is a layer mainly composed of unoxidized Fe having high reactivity with zinc, and accurately controlled for improving wettability of plating and the adhesion of plated layer. The alloyed hot-dip galvanized steel sheet including the A layer according to the present invention containing C, Si, Mn, and the like has a high-strength of 590 MPa or more, and is excellent in the wettability of plating and the adhesion of plated layer.

As shown in FIG. 2, it is necessary to include more than or equal to 50 vol % of the ferrite structure based on a volume of the A layer for obtaining excellent adhesion of plated layer. The ferrite is a structure excellent in ductility.

As described above, in the alloyed hot-dip galvanized steel sheet, the ductility deteriorates with the increase in strength, and along therewith, pressing load at the time of performing press forming is large, so that the shear stress applied to the plated layer from a mold at the time of performing forming increases. Accordingly, the plated layer is easily peeled from the interface with the base steel sheet, and results in defects in corrosion prevention and defects in appearance with press scratches and the like, which may become a problem related to the deterioration in the adhesion of plated layer. However, in the present invention, since the A layer immediately under the plated layer includes a ferrite structure and is excellent in ductility, the problem is solved. If less than 50 vol % of the ferrite structure is included in the A layer, the improvement in the adhesion of plated layer is insufficient. It is preferred that the A layer include more than or equal to 55 vol % of the ferrite structure. The ferrite phase may include a form of an acicular ferrite in addition to a polygonal ferrite.

The inevitable structures included in the balance represent bainite, martensite, residual austenite, and pearlite.

Note that each phase of the structures such as ferrite, martensite, bainite, austenite, pearlite, and residual structures can be identified and their locations and area fraction can be observed and quantitatively measured using an optical microscope having a magnification of 1000 times and a scanning and transmission electron microscope having a magnification of 1000 times to 100000 times after a cross section of the steel sheet in a rolling direction or a cross section in the right angle direction of the rolling direction is etched using a Nital reagent and the reagent as disclosed in JP 59-219473A. In Examples, the area fraction of the ferrite structure can be obtained by observing 20 or more fields and applying the point-count method or image analysis up to the depth of 2 μm from immediately under the surface of the base steel sheet. Then, the average value is determined as the content based on the volume.

Further, it is necessary that the A layer include, based on a mass of the A layer, more than or equal to 90 mass % of unoxidized Fe, less than or equal to 10 mass % of a total of contents of oxides of Fe, Si, Mn, P, S, and Al, and less than 0.05 mass % of C, for obtaining excellent wettability of plating and adhesion of plated layer.

As described above, in the high-strength alloyed hot-dip galvanized steel sheet including Si and Mn, Si and Mn are elements which are more easily oxidizable compared with Fe, so at the time of heating in recrystallization annealing in a conventional Fe-reducing atmosphere, Si and Mn on the surface of the base steel sheet oxidize. Further, Si and Mn which thermally diffuse from the inside of the base steel sheet oxidize at the surface whereby gradually the Si and Mn oxides become concentrated on the surface. If the Si and Mn oxides concentrate at the surface, in the process of dipping the base steel sheet in the hot-dip galvanizing bath, contact between the molten zinc and the base steel sheet would be prevented, which would cause a problem of a drop in the wettability of plating and the adhesion of plated layer of the alloyed hot-dip galvanized layer. In addition, as described above, the internal oxides of Si and Mn written in Patent Literatures are also present in the vicinity of the surface of the inside of the base steel sheet. Accordingly, there is a problem in that the ductility and the bendability of the base steel sheet are deteriorated and the press forming cannot be performed. Further, when the shear stress is applied to the plated layer at the time of performing the press forming, there is a problem related to the adhesion of plated layer that the plated layer peels from the vicinity of the surface of the inside of the base steel sheet in which the internal oxides are present. However, in the present invention, the A layer immediately under the plated layer is mainly composed of Fe, and the oxides of Fe, Si, Mn, P, S, and Al are decreased, so that the problems are solved. The oxides used here may be any of the internal oxides, or external oxides which concentrate on the surface of the base steel sheet. Examples of the oxides include FeO, Fe₂O₃, Fe₃O₄, MnO, MnO₂, Mn₂O₃, Mn₃O₄, SiO₂, P₂O₅, Al₂O₃, SO₂ as single oxides and respective nonstoichiometric compositions of single oxides, or FeSiO₃, Fe₂SiO₄, MnSiO₃, Mn₂SiO₄, AlMnO₃, Fe₂PO₃, Mn₂PO₃ as composite oxides and respective nonstoichiometric compositions of composite oxides.

For the reasons described above, as shown in FIG. 3, the improvement in the wettability of plating and the adhesion of plated layer is insufficient when the content of unoxidized Fe in the A layer is less than 90%. The content of Fe is preferably more than or equal to 92%. Further, as shown in FIG. 4, when the total of the contents of the oxides of Fe, Si, Mn, P, S, and Al exceeds 10%, the improvement in the wettability of plating and the adhesion of plated layer are insufficient. The total of the contents of the oxides of Fe, Si, Mn, P, S, and Al is preferably less than or equal to 8%.

The content of unoxidized Fe in the A layer is determined as follows, for example. The alloyed hot-dip galvanized steel sheet is analyzed in the depth direction using an X-ray photoelectron spectroscope with an ion gun (XPS, PHI5800, manufactured by Ulvac Phi, Inc.), and the content from the depth at which Zn could no longer be detected to the depth of 2 μm further down, which is worked out from a zero-valent Fe spectrum, is averaged by the depth. In the same manner, the total of the contents of the oxides of Fe, Si, Mn, P, S, and Al is determined by finding out the respective contents of Fe, Si, Mn, P, S, and Al from the depths at which Zn could no longer be detected to the depth of 2 μm further down, which are worked out from Fe, Si, Mn, P, S, and Al spectra whose valences are not zero, adding the contents, and then averaging the content by the depth. However, the measurement method is not particularly limited, and the contents may be determined using analysis means as necessary, such as depth direction analysis using glow discharge spectrometry (GDS), secondary ion mass spectrometry (SIMS), and time-of-flight type secondary ion mass spectrometry (TOF-SIMS), and cross-sectional analysis using a transmission electron microscope (TEM) and an electron probe microanalyzer (EPMA).

Further, as described above, in the high-strength alloyed hot-dip galvanized steel sheet containing C, when C is present in a grain boundary or a grain of the base steel sheet in the recrystallization annealing, there is a problem in that the reaction between the molten zinc and the base steel sheet in the process of Fe—Zn alloying reaction after dipping the base steel sheet in the hot-dip galvanizing bath is inhibited, to thereby deteriorate the adhesion of plated layer. In addition, there is also a problem in that the inclusion of C in the alloyed hot-dip galvanized layer after the alloying reaction lowers the ductility of the plating, so that peeling of the plating easily occurs when press forming is performed. However, in the present invention, the content of C in the A layer immediately under the plated layer is extremely reduced, and the problems are solved. For the reasons described above, as shown in FIG. 5, the improvement in the adhesion of plated layer is insufficient when the content of C in the A layer is more than or equal to 0.05%. The content of C in the A layer is less than 0.05%, and is preferably less than or equal to 0.03%.

The content of C in the A layer is determined as follows, for example. The alloyed hot-dip galvanized steel sheet is analyzed in the depth direction using a GDS (GDA750, manufactured by Rigaku Corporation), and the content from the depth at which Zn could no longer be detected to the depth of 2 μm further down is averaged by the depth. However, the measurement method is not particularly limited, and the contents may be determined using analysis means as necessary, such as depth direction analysis using XPS, SIMS, and TOF-SIMS, and cross-sectional analysis using TEM and EPMA.

As shown in FIG. 6, it is necessary that the A layer have a thickness of more than or equal to 2 μm and less than or equal to 20 μm for achieving excellent wettability of plating and adhesion of plated layer. The improvement in the wettability of plating and the adhesion of plated layer is insufficient when the thickness is less than 2 μm, and the strength of the base steel sheet deteriorates when the thickness exceeds 20 μm. The thickness of the A layer is preferably more than or equal to 2 μm and less than or equal to 15 μm.

The thickness of the A layer is determined as follows. That is, vol % of the above-mentioned ferrite structure is measured from immediately under the surface of the base steel sheet, and the depth at which the ferrite structure is less than 50 vol % (depth from immediately under the surface of the base steel sheet) is represented by D1. D2 represents, when the steel sheet is analyzed in the depth direction using an XPS, the depth from the depth at which Zn could no longer be detected to the depth at which the content of Fe is less than 90% determined by the above-mentioned method. D3 represents the depth, which is determined simultaneously with D2 using the XPS, from the depth at which Zn could no longer be detected to the depth at which the total of the contents of Fe, Si, Mn, P, S, and Al in the Fe, Si, Mn, P, S, and Al spectra whose valences are not zero determined by the above-mentioned method exceeds 10%. D4 represents, when the steel sheet is analyzed in the depth direction using a GDS, the depth from the depth at which Zn could no longer be detected to the depth at which the content of C determined by the above-mentioned method is more than or equal to 0.05%. Then, among average values D1(AVE) to D4(AVE) obtained by measuring five points of each of D1 to D4 at positions which are spaced apart from each other by more than or equal to 20 mm and less than or equal to 50 mm, the smallest value is employed as the thickness of the A layer. The thus determined A layer is a layer mainly composed of a ferrite structure containing Fe as a main component, which is decreased in the oxides of Fe, Si, Mn, P, S, and Al, which are external oxides or internal oxides, and is also decreased in C. As long as the A layer has a thickness within the range of the present invention, the A layer is excellent in the wettability of plating and the adhesion of plated layer.

Next, the method of manufacturing the alloyed hot-dip galvanized steel sheet according to the present invention will be described.

The manufacturing method includes subjecting a steel material containing given components to casting, hot-rolling, pickling, and cold rolling, to thereby produce a cold-rolled steel sheet (base steel sheet), subjecting the cold-rolled steel sheet to an annealing treatment in a continuous hot-dip galvanizing plant equipped with a heating furnace and a soaking furnace, and then performing a hot-dip galvanizing treatment and an alloying treatment. In the heating furnace and the soaking furnace in which the annealing treatment is performed, the cold-rolled steel sheet whose temperature is in the range of higher than or equal to 500° C. and lower than or equal to 950° C. while staying in the furnaces is passed under the following conditions, and after that, the cold-rolled steel sheet is subjected to the hot-dip galvanizing treatment and subsequently subjected to the alloying treatment at an alloying heating temperature of higher than or equal to 440° C. and lower than or equal to 600° C. Those conditions are important for manufacturing the alloyed hot-dip galvanized steel sheet excellent in the wettability of plating and the adhesion of plated layer according to the present invention.

Conditions of the heating furnace: an all radiant tube type heating furnace is used, a time period that the temperature of the base steel material is in the range of higher than or equal to 500° C. and lower than or equal to 950° C. is 100 seconds to 1000 seconds, an atmosphere of the heating furnace contains hydrogen, water vapor, and nitrogen, a logarithm log(P_(H2O)/P_(H2)) of a value obtained by dividing a partial water vapor pressure (P_(H2O)) by a partial hydrogen pressure (P_(H2)) is more than or equal to −4.0 and less than −2.0, and a hydrogen concentration is more than or equal to 3 vol % and less than or equal to 30 vol %.

Conditions of the soaking furnace: a time period that the temperature of the base steel material is in the range of higher than or equal to 500° C. and lower than or equal to 950° C. is 100 seconds to 1000 seconds, an atmosphere of the soaking furnace contains hydrogen, water vapor, and nitrogen, a logarithm log(P_(H2O)/P_(H2)) of a value obtained by dividing a partial water vapor pressure (P_(H2O)) by a partial hydrogen pressure (P_(H2)) is more than or equal to −8.0 and less than −4.0, and a hydrogen concentration is more than or equal to 3 vol % and less than or equal to 30 vol %.

In the manufacturing method according to the present invention, the annealing treatment and the treatment of providing the plated layer is performed in the continuous hot-dip galvanizing plant equipped with the all radiant tube type heating furnace. An all radiant tube type heating furnace is resistant to roll pickup and is good in productivity of the annealing treatment.

As shown in FIG. 7 and FIG. 8, regarding the conditions of the heating furnace and the conditions of the soaking furnace, it is necessary that maximum sheet temperature of the passing cold-rolled steel sheet be higher than or equal to 500° C. and lower than or equal to 950° C. for manufacturing the alloyed hot-dip galvanized steel sheet according to the present invention. When the temperature is lower than 500° C., the tensile strength of the base steel sheet is lower than 590 MPa. In addition, naturally oxidized Fe on the surface of the base steel sheet remains after the annealing, to thereby deteriorate the wettability of plating and the adhesion of plated layer. When the temperature exceeds 950° C., excessive thermal energy is required, which is not economical. Further, since the volume fraction of ferrite decreases and the oxides of Si and Mn are excessively formed, the wettability of plating and the adhesion of plated layer deteriorate. The temperature is preferably higher than or equal to 600° C. and lower than or equal to 850° C.

In the heating furnace, a log(P_(H2O)/P_(H2)) of the atmosphere in the furnace is increased to oxidize C, Si, Mn, P, S, and Al on the surface of the base steel sheet. If C is oxidized, C detaches from the base steel sheet as carbon monoxide or carbon dioxide, and hence, the C content on the surface of the base steel sheet can be decreased. Further, Si, Mn, P, S, and Al are internally oxidized immediately under the surface of the base steel sheet. At that time, by controlling the level of the log(P_(H2O)/P_(H2)) appropriately, the oxidation of Fe can be suppressed. Accordingly, the excellent wettability of plating and adhesion of plated layer can be obtained.

As shown in FIG. 7, in the heating furnace, the time period that the temperature of the base steel material is in the range of higher than or equal to 500° C. and lower than or equal to 950° C. is 100 seconds to 1000 seconds. When the time period is less than 100 seconds, the decreased amount of the C content and the amount of internally oxidized Si, Mn, P, S, and Al are small, and hence, the wettability of plating and the adhesion of plated layer deteriorate. When the time period exceeds 1000 seconds, the productivity deteriorates, and the C content is excessively decreased to cause lowering in the tensile strength and to deteriorate the adhesion of plated layer due to excessive internal oxidization and generation of internal stress.

As shown in FIG. 9, in the heating furnace, the atmosphere in which the base steel sheet is in the range of higher than or equal to 500° C. and lower than or equal to 950° C. contains hydrogen, water vapor, and nitrogen, and a logarithm log(P_(H2O)/P_(H2)) of a value obtained by dividing a partial water vapor pressure (P_(H2O)) by a partial hydrogen pressure (P_(H2)) is more than or equal to −4.0 and less than −2.0. When the log(P_(H2O)/P_(H2)) is less than −4.0, the oxidation reaction of C does not sufficiently proceed, and hence, the wettability of plating and the adhesion of plated layer deteriorate. When the log(P_(H2O)/P_(H2)) exceeds 0.0, since Fe oxides excessively form on the surface of the steel sheet, the wettability of plating and the adhesion of plated layer deteriorate. In addition, C in the base material is oxidized and excessively detaches from the base material, which causes lowering in the tensile strength of the base material, and internal stress of the steel sheet increases due to excessive internal oxidization of Si, Mn, P, S, and Al, which causes deterioration in the adhesion of plated layer. When the log(P_(H2O)/P_(H2)) is less than or equal to 0.0, those problems can be avoided, but when the log(P_(H2O)/P_(H2)) is more than or equal to −2.0, the deterioration of a lining of the heating furnace (normally manufactured by SUS Corporation) becomes noticeable, which is not preferable in terms of industry. Accordingly, in the present invention, the log(P_(H2O)/P_(H2)) in the heating furnace is in the range of less than −2.0.

As shown in FIG. 10, the hydrogen concentration in the atmosphere of the heating furnace is more than or equal to 3 vol % and less than or equal to 30 vol %. When the hydrogen concentration is less than 3 vol %, it is difficult to control the hydrogen concentration and the log(P_(H2O)/P_(H2)) varies widely within the furnace. Therefore, the wettability of plating and the adhesion of plated layer deteriorate. When the hydrogen concentration exceeds 30 vol %, the amount of hydrogen to be fed increases, which is not economical. In addition, hydrogen enters inside the steel sheet whereby hydrogen embrittlement occurs, and the steel sheet strength and the adhesion of plated layer deteriorate.

Rate of temperature rise of the sheet in the heating furnace is not particularly limited. However, if the rate is too slow, the productivity deteriorates, and if the rate is too fast, the cost required for the heating plant becomes expensive. Accordingly, the rate is preferably more than or equal to 0.5° C/s and less than or equal to 20° C/s.

Initial temperature of the sheet at the time of entering into the heating furnace is not particularly limited. However, if the temperature is too high, Fe oxides are excessively formed on the base steel sheet and the wettability of plating and the adhesion of plated layer deteriorate, and if the temperature is too low, cost required for the cooling becomes expensive. Accordingly, the temperature is preferably higher than or equal to 0° C. and lower than or equal to 200° C.

Subsequently, conditions of the soaking furnace continued from the heating furnace will be described.

In the soaking furnace, a log(P_(H2O)/P_(H2)) of the atmosphere in the furnace is decreased to reduce the oxides that are formed by the internal oxidization and external oxidization of Si, Mn, P, S, and Al immediately under the surface of the base steel sheet formed in the heating furnace. With sufficient reduction, the excellent wettability of plating and adhesion of plated layer can be obtained.

As shown in FIG. 8, in the soaking furnace, the time period that the temperature of the steel sheet is in the range of higher than or equal to 500° C. and lower than or equal to 950° C. is 100 seconds to 1000 seconds. When the time period is less than 100 seconds, the reduction of the oxides of Si, Mn, P, S, and Al is insufficient, and hence, the wettability of plating and the adhesion of plated layer deteriorate. When the time period exceeds 1000 seconds, the productivity deteriorates, and the C content immediately under the surface of the base steel sheet increases by thermal diffusion of C. Accordingly, the wettability of plating and the adhesion of plated layer deteriorate.

As shown in FIG. 9, in the soaking furnace, the atmosphere in which the steel sheet is in the range of higher than or equal to 500° C. and lower than or equal to 950° C. contains hydrogen, water vapor, and nitrogen, and a logarithm log(P_(H2O)/P_(H2)) of a value obtained by dividing a partial water vapor pressure (P_(H2O)) by a partial hydrogen pressure (P_(H2)) is more than or equal to −8.0 and less than −4.0. When the log(P_(H2O)/P_(H2)) is less than −8.0, in addition to that it is poor in industrial practicality, in the case where ceramics are used for the furnace body, the ceramics are reduced and lower the lifetime of the furnace. When the log(P_(H2O)/P_(H2)) is more than or equal to −4.0, the reduction of Si, Mn, P, S, and Al is insufficient, and Si, Mn, and Al externally oxidize, so that the wettability of plating and the adhesion of plated layer deteriorate. In addition, C in the base steel sheet detaches from the base steel sheet by an oxidation reaction, which causes lowering in the tensile strength of the base steel sheet. The log(P_(H2O)/P_(H2)) of the atmosphere of the soaking furnace is more preferably more than or equal to −7.0 and less than −4.0.

As shown in FIG. 10, the hydrogen concentration in the atmosphere of the soaking furnace is more than or equal to 3 vol % and less than or equal to 30 vol %. When the hydrogen concentration is less than 3 vol %, it is difficult to control the hydrogen concentration, and the log(P_(H2O)/P_(H2)) varies widely within the furnace, so that the wettability of plating and the adhesion of plated layer deteriorate. When the hydrogen concentration exceeds 30 vol %, the amount of hydrogen to be fed increases, which is not economical. In addition, hydrogen enters inside the steel sheet whereby hydrogen embrittlement occurs, and the steel sheet strength and the adhesion of plated layer deteriorate.

Individual control of the atmospheric conditions in the heating furnace and the soaking furnace of the continuous hot-dip galvanizing plant is a characteristic feature of the method of manufacturing the hot-dip galvanized steel sheet of the present invention. For individual control, it is necessary to charge the furnaces with nitrogen, water vapor, and hydrogen while controlling the concentrations thereof. Further, the log(P_(H2O)/P_(H2)) of the oxygen potential in the heating furnace has to be higher than the log(P_(H2O)/P_(H2)) of the oxygen potential in the soaking furnace. For this reason, when gas flows from the heating furnace toward the soaking furnace, an additional atmosphere of a higher hydrogen concentration or lower water vapor concentration than the inside of the heating furnace may be introduced from between the heating furnace and the soaking furnace toward the soaking furnace. When gas flows from the soaking furnace toward the heating furnace, an additional atmosphere of a lower hydrogen concentration or higher water vapor concentration than the inside of the soaking furnace may be introduced from between the heating furnace and soaking furnace toward the heating furnace.

After the base steel sheet leaves the heating furnace and the soaking furnace, the base steel sheet can be run through the general ordinary steps until being dipped in the hot-dip galvanizing bath. For example, the base steel sheet can be run through a slow cooling step, a rapid cooling step, an overaging step, a second cooling step, a water quench step, a reheating step, and the like alone or in any combination. It is also possible to similarly run the base steel sheet through general ordinary steps after dipping in a hot-dip galvanizing bath.

The base steel sheet is run through the heating furnace and the soaking furnace, then is cooled and, in accordance with need, held in temperature, is dipped in a hot-dip galvanizing bath where it is hot-dip galvanized, then is subjected to alloying treatment in accordance with need.

With hot-dip galvanizing treatment, it is preferred to use a hot-dip galvanizing bath which has a bath temperature of higher than or equal to 440° C. and lower than 550° C., a concentration of Al in the bath of more than or equal to 0.08% and less than or equal to 0.24%, and inevitable impurities.

When the bath temperature is lower than 440° C., the molten zinc in the bath may solidify, so it becomes difficult to control the amount of adhesion of the plating. When the bath temperature exceeds 550° C., the evaporation of the molten zinc at the bath surface becomes immense, the operating cost rises, and vaporized zinc sticks to the inside of the furnace, so there are problems in operation.

When the hot-dip galvanized steel sheet is subjected to the plating treatment, if the concentration of Al in the bath becomes less than 0.08%, a large amount of layer is formed and the adhesion of plated layer deteriorates, while if the concentration of Al in the bath exceeds 0.24%, the Al which oxidizes in the bath or on the bath increases and the wettability of plating deteriorates.

As shown in FIG. 11, when performing hot-dip galvanizing treatment, then alloying treatment, it is necessary that the alloying treatment be performed at higher than or equal to 440° C. and lower than or equal to 600° C. When the temperature is lower than 440° C., the alloying proceeds slowly. When the temperature exceeds 600° C., due to overalloying, a hard, brittle Zn—Fe alloy layer is overly formed at the interface with the base steel sheet, and the adhesion of plated layer deteriorates. Further, when the temperature exceeds 600° C., the residual austenite phase of the base steel sheet breaks down, so the balance of strength and ductility of the base steel sheet also deteriorates.

EXAMPLES

Hereinafter, the present invention will be specifically described by way of Examples.

Test materials 1 to 94, which are shown in Tables 1 (Table 1-1, Table 1-2), were prepared, the test materials 1 to 94 having been subjected to the usual casting, hot-rolling, pickling, and cold rolling, and each being a cold-rolled steel sheet (base steel sheet) having a thickness of 1 mm. Some of the test materials 1 to 94 were appropriately selected and were subjected to an annealing treatment, a hot-dip galvanizing treatment, and an alloying treatment under the conditions of Tables 2 and Tables 3, in a continuous hot-dip galvanizing plant equipped with an all radiant tube type heating furnace of a relatively high productivity heating method with little roll pickup as explained above. By using an all radiant tube type of furnace, as explained above, there is little roll pickup and the productivity is also good.

After the soaking furnace, the base steel sheet was treated by general slow cooling, rapid cooling, overaging, and second cooling steps and then was dipped in a hot-dip galvanizing bath. The hot-dip galvanizing bath had a plating bath temperature of 460° C. and contained 0.13% of Al and 0.03% of Fe in addition to Zn. After the base steel sheet was dipped in the hot-dip galvanizing bath, the base steel sheet was wiped by nitrogen gas to adjust the plating thickness. After that, the base steel sheet was subjected to an alloying treatment by being heated in an alloying furnace for 30 seconds. The obtained alloyed hot-dip galvanized steel sheet was evaluated for wettability of plating and adhesion of plated layer. Tables 2 show the results of Examples, and Tables 3 show results of Comparative Examples.

The wettability of plating was evaluated by mapping Zn and Fe on any 200 μm×200 μm area of 10 locations that are spaced apart from each other by 1 mm or more on the surface of the plated steel sheet of the alloyed hot-dip galvanized steel sheet by EPMA. The wettability of plating was evaluated as follows. Regarding the case where there is no Zn and Fe is exposed, the case where there are four or more locations out of 10 locations was evaluated as poor in the wettability of plating (Poor), the case where there are one to three locations out of 10 locations was evaluated as good in the wettability of plating (Good), and the case where no such location was evaluated as excellent in the wettability of plating (Excellent). “Good” and “Excellent” were each evaluated as pass in the wettability of plating and “Poor” was evaluated as fail in the wettability of plating.

The adhesion of plated layer was measured by a powdering test. The case where a peeled length exceeds 2 mm was evaluated as poor in the adhesion of plated layer (Poor), the case where a peeled length was less than or equal to 2 mm and more than 1 mm was evaluated as good in the adhesion of plated layer (Good), and the case where a peeled length was less than or equal to 1 mm was evaluated as excellent in the adhesion of plated layer (Excellent). The powdering test is a method of examination of adhesion involving sticking Cellotape (registered trademark) to the alloyed hot-dip galvanized steel sheet, bending the tape surface at R=1, 90° C., unbending the tape, then peeling off the tape, and measuring the peeled length of the alloyed hot-dip galvanized steel sheet.

A tensile test was performed by sampling a JIS No. 5 test piece from an alloyed hot-dip galvanized steel sheet having a thickness of 1.0 mm in directions vertical to and parallel to the rolling direction to evaluate tensile properties. The tensile test was performed on each of five test pieces in the vertical direction and in the parallel direction, and an average value of the results was determined as a tensile strength (TS). Note that, as for a steel sheet having large material anisotropy, there was a tendency that the elongation values varied.

As shown in Tables 2 (Table 2-1, Table 2-2, Table 2-3, and Table 2-4) and Tables 3 (Table 3-1 and Table 3-2), it was found out that the wettability of plating and the adhesion of plated layer of Examples (Tables 2) according to the present invention were excellent compared to Comparative Examples (Tables 3). Note that, when the log(P_(H2O)/P_(H2)) in the heating furnace is in the range of more than or equal to −4.0 and less than or equal to 0.0, the wettability of plating and the adhesion of plated layer were better compared to Comparative Example, but when the log(P_(H2O)/P_(H2)) is more than or equal to −2.0, the deterioration of a lining of the heating furnace (normally manufactured by SUS Corporation) became noticeable.

TABLE 1-1 Composition [wt %] No. C Si Mn P S Al N Other selected element(s) Test material 1 0.06 0.5 2.5 0.050 0.004 0.20 0.002 Test material 2 0.06 0.5 3.5 0.050 0.004 0.20 0.002 Test material 3 0.06 0.3 4.5 0.050 0.004 0.20 0.002 Test material 4 0.06 1.0 2.5 0.050 0.004 0.20 0.002 Test material 5 0.06 1.0 3.5 0.050 0.004 0.20 0.002 Test material 6 0.06 1.0 4.5 0.050 0.004 0.20 0.002 Test material 7 0.06 1.5 0.5 0.050 0.004 0.20 0.002 Test material 8 0.06 1.5 3.5 0.050 0.004 0.20 0.002 Test material 9 0.06 1.5 4.5 0.050 0.004 0.20 0.002 Test material 10 0.06 2.5 0.5 0.050 0.004 0.20 0.002 Test material 11 0.06 2.5 1.5 0.050 0.004 0.20 0.002 Test material 12 0.06 2.5 2.5 0.050 0.004 0.20 0.002 Test material 13 0.06 2.5 3.5 0.050 0.004 0.20 0.002 Test material 14 0.06 2.5 4.5 0.050 0.004 0.20 0.002 Test material 15 0.1 0.5 0.5 0.005 0.001 0.04 0.002 Test material 16 0.1 0.5 1.5 0.005 0.001 0.04 0.002 Test material 17 0.1 0.5 2.5 0.005 0.001 0.04 0.002 Test material 18 0.1 0.5 3.5 0.005 0.001 0.04 0.002 Test material 19 0.1 0.5 4.5 0.005 0.001 0.04 0.002 Test material 20 0.1 1.0 0.5 0.005 0.001 0.04 0.002 Test material 21 0.1 1.0 1.5 0.005 0.001 0.04 0.002 Test material 22 0.1 1.0 2.5 0.005 0.001 0.04 0.002 Test material 23 0.1 1.0 3.5 0.005 0.001 0.04 0.002 Test material 24 0.1 1.0 4.5 0.005 0.001 0.04 0.004 Test material 25 0.1 1.5 0.5 0.005 0.001 0.04 0.004 Test material 26 0.1 1.5 1.5 0.005 0.001 0.04 0.004 Test material 27 0.1 1.5 2.5 0.005 0.001 0.04 0.004 Test material 28 0.1 1.5 3.5 0.005 0.001 0.04 0.004 Test material 29 0.1 1.5 4.5 0.005 0.001 0.04 0.004 Test material 30 0.1 2.5 0.5 0.005 0.001 0.04 0.004 Test material 31 0.1 2.5 1.5 0.005 0.001 0.04 0.004 Test material 32 0.1 2.5 2.5 0.005 0.001 0.04 0.004 Test material 33 0.1 2.5 3.5 0.005 0.001 0.04 0.004 Test material 34 0.1 2.5 4.5 0.005 0.001 0.04 0.002 Test material 35 0.2 0.5 0.5 0.001 0.0005 0.01 0.002 Test material 36 0.2 0.3 1.5 0.001 0.0005 0.01 0.002 Test material 37 0.2 0.3 2.5 0.001 0.0005 0.01 0.002 Test material 38 0.2 0.5 3.5 0.001 0.0005 0.01 0.002 Test material 39 0.2 0.5 4.5 0.001 0.0005 0.01 0.002 Test material 40 0.2 1.0 0.5 0.001 0.0005 0.01 0.002 Test material 41 0.2 1.0 1.5 0.001 0.0005 0.01 0.002 Test material 42 0.2 1.0 2.5 0.001 0.0005 0.01 0.002 Test material 43 0.2 1.0 3.5 0.001 0.0005 0.01 0.002 Test material 44 0.2 1.0 4.5 0.001 0.0005 0.01 0.002 Test material 45 0.2 1.5 0.5 0.001 0.0005 0.01 0.002 Test material 46 0.2 1.5 1.5 0.001 0.0005 0.01 0.002 Test material 47 0.2 1.5 2.5 0.001 0.0005 0.01 0.002

TABLE 1-2 Composition [wt %] No. C Si Mn P S Al N Other selected element(s) Test material 48 0.2 1.5 3.5 0.001 0.0005 0.01 0.002 Test material 49 0.2 1.5 4.5 0.001 0.0005 0.01 0.002 Test material 50 0.2 2.5 0.5 0.001 0.0005 0.01 0.002 Test material 51 0.2 2.5 1.5 0.001 0.0005 0.01 0.002 Test material 52 0.2 2.5 2.5 0.001 0.0005 0.01 0.002 Test material 53 0.2 2.5 3.5 0.001 0.0005 0.01 0.002 Test material 54 0.2 2.5 4.5 0.001 0.0005 0.01 0.002 Test material 55 0.4 0.5 0.5 0.001 0.001 0.005 0.002 Test material 56 0.4 0.5 1.5 0.001 0.001 0.005 0.002 Test material 57 0.4 0.5 2.5 0.001 0.001 0.005 0.002 Test material 58 0.4 0.5 3.5 0.001 0.001 0.005 0.002 Test material 59 0.4 0.5 4.5 0.001 0.001 0.005 0.002 Test material 60 0.4 1.0 0.5 0.001 0.001 0.005 0.002 Test material 61 0.4 1.0 1.5 0.001 0.001 0.005 0.002 Test material 62 0.4 1.0 2.5 0.001 0.001 0.005 0.002 Test material 63 0.4 1.0 3.5 0.001 0.001 0.005 0.002 Test material 64 0.4 1.0 4.5 0.001 0.001 0.005 0.002 Test material 65 0.4 1.5 0.5 0.001 0.001 0.005 0.002 Test material 66 0.4 1.5 1.5 0.001 0.001 0.005 0.002 Test material 67 0.4 1.5 2.5 0.001 0.001 0.005 0.002 Test material 68 0.4 1.5 3.5 0.001 0.001 0.005 0.002 Test material 69 0.4 1.5 4.5 0.001 0.001 0.005 0.002 Test material 70 0.4 2.5 0.5 0.001 0.001 0.005 0.002 Test material 71 0.4 2.5 1.5 0.001 0.001 0.005 0.002 Test material 72 0.4 2.5 2.5 0.001 0.001 0.005 0.002 Test material 73 0.4 2.5 3.5 0.001 0.001 0.005 0.002 Test material 74 0.4 2.5 4.5 0.001 0.001 0.005 0.002 Test material 75 0.2 1.5 2.5 0.005 0.001 0.04 0.002 Cr: 0.2 Test material 76 0.2 1.5 2.5 0.005 0.001 0.04 0.002 Ni: 0.2 Test material 77 0.2 1.5 2.5 0.005 0.001 0.04 0.002 Cu: 0.2 Test material 78 0.2 1.5 2.5 0.005 0.001 0.04 0.002 Nb: 0.02 Test material 79 0.2 1.5 2.5 0.005 0.001 0.04 0.002 Ti: 0.02 Test material 80 0.2 1.5 2.5 0.005 0.001 0.04 0.002 V: 0.02 Test material 81 0.2 1.5 2.5 0.005 0.001 0.04 0.002 B: 0.002 Test material 82 0.2 1.5 2.5 0.005 0.001 0.04 0.002 Ca: 0.002 Test material 83 0.2 1.5 2.5 0.005 0.001 0.04 0.002 Mg: 0.002 Test material 84 0.2 1.5 2.5 0.005 0.001 0.04 0.002 La: 0.002 Test material 85 0.2 1.5 2.5 0.005 0.001 0.04 0.002 Ce: 0.002 Test material 86 0.2 1.5 2.5 0.005 0.001 0.04 0.002 Y: 0.002 Test material 87 0.2 1.5 2.5 0.005 0.001 0.04 0.002 Cr: 0.1, Ni: 0.1 Test material 88 0.2 1.5 2.5 0.005 0.001 0.04 0.002 Cr: 0.1, B: 0.005 Test material 89 0.2 1.5 2.5 0.005 0.001 0.04 0.002 Cu: 0.1, Mg: 0.001 Test material 90 0.2 1.5 2.5 0.005 0.001 0.04 0.002 Nb: 0.001, Ti: 0.001 Test material 91 0.2 1.5 2.5 0.005 0.001 0.04 0.002 V: 0.01, La: 0.001 Test material 92 0.2 1.5 2.5 0.005 0.001 0.04 0.002 Cr: 0.5, Ce: 0.001 Test material 93 0.2 1.5 2.5 0.005 0.001 0.04 0.002 Cr: 0.1, Ti: 0.001, B: 0.0005 Test material 94 0.2 1.5 2.5 0.005 0.001 0.04 0.002 Cr: 0.7, Nb: 0.004, Ti: 0.004

TABLE 2-1 Recrystallization annealing conditions Heating furnace conditions Soaking pit conditions Time Time period that period that temperature temperature of cold- of cold- rolled steel rolled steel sheet is in sheet is in temperature temperature range of range of 500° C. to 500° C. to Cold- Maximum 950° C. in Maximum 950° C. in rolled sheet heating Oxygen Hydrogen sheet soaking Oxygen Hydrogen steel temperature furnace potential concentration temperature pit potential concentration No. sheet [° C.] [sec] logP_(H2O)/P_(H2) [vol %] [° C.] [sec] logP_(H2O)/P_(H2) [vol %] A1 Test material 1 675 253 −1.4 19 675 297 −6.1 3 A2 Test material 3 852 442 −2.4 26 854 510 −5.2 27 A3 Test material 4 813 356 −2.2 9 814 707 −7.3 15 A4 Test material 6 720 421 −2.3 4 723 199 −6.1 6 A5 Test material 7 778 967 −1.5 15 780 421 −7.2 15 A6 Test material 9 738 279 −3.0 19 739 251 −6.0 18 A7 Test material 10 725 698 −2.7 20 725 274 −7.5 23 A8 Test material 13 678 487 −0.7 22 681 444 −4.7 27 A9 Test material 14 716 218 −3.4 16 719 403 −6.7 23 A10 Test material 15 616 144 −3.2 16 618 110 −7.4 16 A11 Test material 16 669 210 −3.5 21 670 753 −6.5 24 A12 Test material 18 726 756 −1.5 22 728 560 −7.4 9 A13 Test material 20 815 438 −2.6 28 816 714 −5.6 3 A14 Test material 21 612 291 −1.5 5 614 703 −5.3 8 A15 Test material 22 754 462 −2.9 11 756 604 −5.6 13 A16 Test material 24 638 157 −2.4 16 641 610 −5.3 9 A17 Test material 26 826 442 −3.3 4 828 573 −7.3 26 A18 Test material 27 856 725 −1.4 11 857 600 −4.2 18 A19 Test material 29 793 336 −1.6 15 795 765 −6.4 22 A20 Test material 30 775 302 −2.5 24 777 613 −6.1 4 A21 Test material 31 766 285 −2.6 18 768 257 −6.7 16 A22 Test material 32 800 329 −3.1 29 801 609 −5.9 22 A23 Test material 34 843 319 −1.3 16 844 299 −5.9 3 A24 Test material 36 826 856 −2.6 14 829 187 −6.3 10 A25 Test material 37 647 506 −2.9 22 649 397 −4.4 13 A26 Test material 38 670 328 −0.8 15 671 182 −6.4 27 A27 Test material 39 736 716 −3.2 13 738 645 −6.9 7 A28 Test material 40 634 275 −2.0 19 635 196 −5.0 26 A29 Test material 41 856 398 −2.1 12 859 813 −6.6 17 A30 Test material 42 696 240 −2.7 5 697 465 −6.8 5 A31 Test material 43 899 666 −1.8 15 901 251 −6.9 5 A32 Test material 44 686 357 −2.0 4 687 622 −4.7 10 A33 Test material 45 712 277 −2.1 15 712 315 −6.9 26 A34 Test material 47 854 425 −1.8 15 857 195 −6.2 13 A35 Test material 49 625 361 −2.2 26 626 467 −6.7 12 A36 Test material 50 717 228 −2.6 21 718 537 −7.0 25 A37 Test material 51 858 506 −2.4 25 861 418 −4.5 20 A38 Test material 52 748 468 −3.0 13 749 187 −4.8 18

TABLE 2-2 Recrystallization annealing conditions Heating furnace conditions Soaking pit conditions Time Time period that period that temperature temperature of cold- of cold- rolled steel rolled steel sheet is in sheet is in temperature temperature range of range of 500° C. to 500° C. to Cold- Maximum 950° C. in Maximum 950° C. in rolled sheet heating Oxygen Hydrogen sheet soaking Oxygen Hydrogen steel temperature furnace potential concentration temperature pit potential concentration No. sheet [° C.] [sec] logP_(H2O)/P_(H2) [vol %] [° C.] [sec] logP_(H2O)/P_(H2) [vol %] A39 Test material 53 672 201 −3.1 12 675 430 −6.7 9 A40 Test material 54 812 409 −3.5 3 813 385 −6.0 13 A41 Test material 55 883 531 −1.6 21 883 801 −5.4 23 A42 Test material 56 869 420 −2.8 22 871 836 −6.3 12 A43 Test material 57 825 372 −2.3 18 826 724 −6.0 23 A44 Test material 58 628 292 −3.4 6 630 473 −5.1 9 A45 Test material 59 899 657 −2.7 3 900 536 −4.8 12 A46 Test material 60 631 154 −1.8 21 631 477 −6.9 14 A47 Test material 61 716 230 −2.3 11 716 213 −5.3 18 A48 Test material 63 729 305 −3.1 28 730 496 −6.9 23 A49 Test material 64 818 500 −3.2 7 821 523 −6.0 13 A50 Test material 65 843 410 −3.2 12 843 389 −4.6 7 A51 Test material 66 834 378 −0.9 17 836 673 −5.3 13 A52 Test material 67 702 368 −3.1 3 703 560 −4.8 14 A53 Test material 68 708 320 −3.1 11 710 191 −4.9 27 A54 Test material 69 611 198 −3.1 8 611 733 −4.9 23 A55 Test material 71 824 667 −1.1 16 826 576 −6.7 16 A56 Test material 72 648 207 −1.4 19 651 199 −5.7 4 A57 Test material 74 767 519 −1.6 23 769 600 −5.5 9 A58 Test material 76 842 606 −0.9 7 844 687 −5.0 17 A59 Test material 77 882 368 −2.3 9 883 357 −6.8 22 A60 Test material 78 894 824 −2.7 4 894 581 −6.0 12 A61 Test material 79 656 552 −2.4 12 657 370 −6.0 27 A62 Test material 80 726 753 −2.1 19 727 203 −4.6 15 A63 Test material 81 755 664 −3.3 7 756 411 −4.7 10 A64 Test material 82 820 514 −0.8 21 820 223 −4.7 16 A65 Test material 83 888 781 −0.9 22 890 857 −4.9 25 A66 Test material 84 699 315 −2.7 14 699 459 −4.8 29 A67 Test material 85 614 338 −1.5 25 617 755 −6.1 16 A68 Test material 86 634 171 −1.7 8 637 554 −4.9 11 A69 Test material 87 821 386 −1.5 7 823 783 −4.5 11 A70 Test material 88 773 323 −0.7 24 774 785 −5.7 7 A71 Test material 89 841 444 −1.8 19 843 343 −4.2 4 A72 Test material 90 803 374 −3.2 22 804 275 −4.6 24 A73 Test material 91 664 240 −2.3 13 665 239 −6.4 29 A74 Test material 92 825 519 −1.0 27 827 294 −6.8 5 A75 Test material 93 798 327 −3.2 24 799 399 −5.6 20 A76 Test material 94 632 158 −2.9 12 634 176 −6.5 9

TABLE 2-3 A layer immediately under surface of substrate steel sheet Alloyed hot-dip Total of Evaluation Alloying galvanized layer Unoxidized contents of adhesion treatment Tensile Fe Ferrite Fe oxides of Fe, wettability of temperature strength content Thickness Thickness content content Si, Mn, P, S, C of plated No. [° C.] [MPa] [wt %] [μm] [μm] [vol %] [wt %] and Al [wt %] content plating layer Remark A1 480 860 11 5 11 66 95 3.4 0.012 Excellent Excellent Example A2 513 738 10 5 10 76 95 3.9 0.016 Excellent Excellent Example A3 562 668 11 4 11 55 92 6.3 0.017 Good Good Example A4 568 807 12 5 12 54 93 5.5 0.008 Excellent Excellent Example A5 537 830 11 6 19 82 91 7.5 0.009 Good Good Example A6 454 739 7 8 7 56 93 6.8 0.017 Excellent Excellent Example A7 554 785 13 6 18 53 93 5.9 0.016 Good Good Example A8 500 639 6 4 6 54 94 4.5 0.014 Excellent Good Example A9 574 1067 11 5 11 58 93 6.7 0.006 Excellent Excellent Example A10 476 1000 15 4 17 56 95 4.2 0.010 Good Good Example A11 459 727 9 6 9 55 96 1.9 0.017 Excellent Excellent Example A12 569 608 13 10 13 58 92 5.8 0.010 Good Good Example A13 488 865 13 10 13 63 93 6.2 0.022 Excellent Excellent Example A14 524 673 14 6 11 73 95 4.5 0.025 Excellent Excellent Example A15 510 752 9 3 9 68 91 7.4 0.017 Excellent Good Example A16 475 961 15 7 18 59 96 2.2 0.020 Excellent Good Example A17 477 912 14 8 17 51 96 2.4 0.011 Good Good Example A18 536 809 14 4 13 88 92 6.4 0.020 Excellent Excellent Example A19 502 998 12 6 12 79 91 7.4 0.014 Excellent Good Example A20 509 903 8 6 6 61 95 3.2 0.008 Excellent Excellent Example A21 520 1047 11 10 11 57 95 4.3 0.025 Excellent Good Example A22 500 638 13 4 13 57 94 3.6 0.016 Excellent Excellent Example A23 578 716 14 8 14 95 95 3.9 0.015 Excellent Excellent Example A24 581 906 6 5 5 78 95 4.7 0.024 Excellent Good Example A25 535 1001 14 9 14 64 95 3.1 0.016 Excellent Excellent Example A26 543 882 11 5 11 93 97 1.3 0.011 Excellent Good Example A27 550 727 8 7 5 60 95 4.8 0.026 Good Excellent Example A28 477 830 12 7 12 65 96 2.4 0.017 Excellent Good Example A29 543 847 9 5 9 69 92 6.8 0.015 Excellent Excellent Example A30 526 695 10 5 10 76 92 7.3 0.015 Excellent Excellent Example A31 570 1089 7 4 4 56 93 5.1 0.019 Excellent Good Example A32 454 913 9 7 9 81 93 5.7 0.016 Excellent Excellent Example A33 544 909 14 9 14 78 94 4.9 0.025 Excellent Good Example A34 523 603 13 7 13 56 95 4.0 0.028 Excellent Good Example A35 460 717 7 6 3 60 94 5.7 0.025 Excellent Excellent Example A36 500 1027 13 7 13 55 97 2.3 0.021 Good Good Example A37 456 642 10 10 10 69 93 6.9 0.015 Excellent Excellent Example A38 460 978 13 6 3 82 95 4.5 0.021 Excellent Good Example

TABLE 2-4 A layer immediately under surface of substrate steel sheet Alloyed hot-dip Total of Evaluation Alloying galvanized layer contents of adhesion treatment Tensile Fe Ferrite Unoxidized oxides of Fe, wettability of temperature strength content Thickness Thickness content Fe content Si, Mn, P, S, C of plated No. [° C.] [MPa] [wt %] [μm] [μm] [vol %] [wt %] and Al [wt %] content plating layer Remark A39 507 787 14 8 14 63 93 6.8 0.016 Excellent Excellent Example A40 566 657 6 8 4 54 97 1.4 0.019 Excellent Good Example A41 550 906 14 8 13 83 93 5.4 0.033 Excellent Excellent Example A42 556 662 12 8 12 62 93 7.3 0.024 Excellent Excellent Example A43 537 796 11 5 11 69 95 3.9 0.023 Excellent Good Example A44 453 954 15 8 14 58 92 6.4 0.023 Excellent Excellent Example A45 501 714 7 22 7 62 93 4.9 0.023 Excellent Good Example A46 501 759 11 17 11 74 94 4.7 0.030 Excellent Excellent Example A47 480 689 14 24 17 78 96 4.2 0.035 Excellent Good Example A48 584 1010 10 28 10 65 97 1.9 0.033 Excellent Excellent Example A49 566 812 14 11 18 65 96 4.2 0.039 Excellent Good Example A50 471 1077 10 18 10 61 94 5.3 0.030 Excellent Excellent Example A51 548 1026 13 17 13 99 91 7.4 0.033 Excellent Good Example A52 523 867 12 21 12 65 95 3.3 0.035 Good Excellent Example A53 524 595 8 10 5 60 93 5.2 0.039 Excellent Good Example A54 498 907 9 12 9 63 94 5.4 0.032 Excellent Excellent Example A55 489 749 7 27 7 56 93 5.9 0.024 Excellent Good Example A56 452 843 11 15 11 90 94 3.9 0.022 Excellent Excellent Example A57 515 732 9 13 9 55 93 5.7 0.027 Excellent Excellent Example A58 485 914 13 9 13 70 93 7.3 0.017 Excellent Good Example A59 526 625 13 15 13 72 94 4.5 0.013 Excellent Excellent Example A60 590 1055 12 10 12 60 92 7.5 0.022 Excellent Good Example A61 528 944 11 12 11 65 95 5.1 0.020 Excellent Excellent Example A62 585 981 8 26 8 57 95 3.8 0.019 Good Good Example A63 571 988 10 7 10 56 94 5.1 0.020 Excellent Excellent Example A64 503 1083 9 17 9 67 95 3.8 0.015 Excellent Good Example A65 457 990 10 11 10 68 94 4.0 0.023 Excellent Excellent Example A66 555 810 14 11 14 74 96 4.2 0.023 Excellent Excellent Example A67 578 826 14 13 14 54 96 3.6 0.012 Excellent Good Example A68 471 849 13 14 13 78 95 3.9 0.010 Excellent Excellent Example A69 565 948 12 14 12 69 93 5.6 0.010 Excellent Good Example A70 526 598 13 7 13 95 96 2.7 0.016 Excellent Excellent Example A71 561 1007 14 10 14 71 92 6.6 0.028 Excellent Good Example A72 530 771 7 20 3 63 92 6.8 0.015 Good Excellent Example A73 538 705 8 20 5 77 93 6.5 0.011 Excellent Excellent Example A74 569 978 8 26 8 88 95 4.1 0.025 Excellent Good Example A75 570 967 14 16 14 82 92 6.7 0.018 Excellent Excellent Example A76 473 827 14 9 15 57 95 3.0 0.027 Excellent Good Example

TABLE 3-1 Recrystallization annealing conditions Heating furnace conditions Soaking pit conditions Time Time period that period that temperature temperature of cold- of cold- rolled steel rolled steel sheet is in sheet is in temperature temperature range of range of 500° C. to 500° C. to Maximum 950° C. in Maximum 950° C. in sheet heating Oxygen Hydrogen sheet soaking Oxygen Hydrogen Cold-rolled temperature furnace potential concentration temperature pit potential concentration No. steel sheet [° C.] [sec] logP_(H2O)/P_(H2) [vol %] [° C.] [sec] logP_(H2O)/P_(H2) [vol %] B1 Test material 1 479  0 −1.5 19 621 115 −6.5 19 B2 Test material 3 621 115 −1.6 15 433  0 −7.2 15 B3 Test material 5 483  0 −4.2 24 485  0 −3.2 24 B4 Test material 7 963 313 −2.2  9 878 251 −7.4  9 B5 Test material 9 921 856 −1.1 12 978 351 −6.8 12 B6 Test material 11 991 1050  −2.3  6 989 542 −3.8  6 B7 Test material 13 778 278   0.3 15 780 421 −6.0 15 B8 Test material 17 738 238 −4.3 19 739 251 −7.0 19 B9 Test material 19 725 225 −1.3 20 725 274 −8.3 20 B10 Test material 21 658 158   0.2 23 659 708 −8.5 23 B11 Test material 27 716 216 −4.7 16 719 403 −3.2 16 B12 Test material 29 616 116 −3.2  1 618  70 −7.4 10 B13 Test material 31 669 169 −3.5 35 670 753 −6.5  1 B14 Test material 33 612 112 −1.0 32 615 242 −6.0 35 B15 Test material 35 726 226 −1.5 12 728 560 −7.4  1 B16 Test material 37 778 278 −1.7  7 780 835 −4.9 38 B17 Test material 39 815 315 −2.6 24 816 714 −5.6 24 B18 Test material 41 612 112 −1.5  7 614 703 −5.3  7 B19 Test material 43 754 254 −2.9 11 756 604 −5.6 11 B20 Test material 45 879 379 −1.6 17 881 761 −6.4 17 B21 Test material 47 638 138 −2.4 16 641 610 −5.3 16 B22 Test material 49 855 355 −0.5 10 856 711 −4.2 10 B23 Test material 51 826 326 −3.3  6 828 573 −7.3  6 B24 Test material 53 856 356 −1.4 11 857 600 −4.2 11 B25 Test material 55 782 282 −0.9 24 783 314 −4.3 24 B26 Test material 57 793 293 −1.6 15 795 765 −6.4 15 B27 Test material 59 775 275 −2.5 24 777 613 −6.1 24 B28 Test material 61 766  35 −1.5 18 768 257 −6.7 18 B29 Test material 63 800  92   0.2  8 795 195 −5.9 25 B30 Test material 65 793 1061    0.5 16 844 299 −6.5  8 B31 Test material 67 843 1030  −1.3 22 701 315 −5.9 16 B32 Test material 69 700 1120  −2.6 14 829 1011  −4.6 22 B33 Test material 71 826  79 −3.1 25 801 1097  −6.3 14 B34 Test material 73 647  35 −4.5 15 671  91 −4.4 22 B35 Test material 75 670  82 −4.7 19 635 1013  −6.4 15 B36 Test material 77 736 1013  −2.1 12 859 1058  −6.9 13 B37 Test material 79 634 196 −2.7  8 697 1101  −5.0 19 B38 Test material 81 856 147 −2.9 22 649  62 −6.6 12 B39 Test material 83 696 236 −4.8 13 738  35 −6.8  8 Note: Underlined value is out of range of the present invention.

TABLE 3-2 A layer immediately under surface of substrate steel sheet Alloyed hot-dip Total of Alloying galvanized layer contents of Evaluation treatment Tensile Fe Thick- Thick- Ferrite Unoxidized oxides of Fe, wettability adhesion temperature strength content ness ness content Fe content Si, Mn, P, S, of of plated No. [° C.] [MPa] [wt %] [μm] [μm] [vol %] [wt %] and Al [wt %] C content plating layer Remark B1 480 567 11 5 0 35 86 12.0  0.052 Poor Poor Comparative Example B2 582 561  8 4 0 42 85 13.0  0.055 Poor Poor Comparative Example B3 513 523 10 5 0 35 82 15.0  0.057 Poor Poor Comparative Example B4 562 668 11 4 0 55 73 25.0  0.017 Poor Poor Comparative Example B5 554 743 11 4 0 51 77 21.0  0.013 Poor Poor Comparative Example B6 568 807 12 5 0 54 84 15.0  0.008 Poor Poor Comparative Example B7 537 533 11 6 0 89 86 12.0  0.009 Poor Poor Comparative Example B8 454 739  7 8 0 37 75 23.0  0.075 Poor Poor Comparative Example B9 554 785 13 6 0 64 77 21.0  0.080 Poor Poor Comparative Example B10 690 664 10 7 0 76 75 23.0  0.019 Poor Poor Comparative Example B11 574 1067  11 5 0 25 78 21.0  0.065 Poor Poor Comparative Example B12 476 1000  15 4 15  56 94 4.2 0.010 Good Poor Comparative Example B13 459 727  9 6 9 55 97 1.9 0.017 Good Poor Comparative Example B14 516 868 10 5 10  84 92 5.1 0.008 Good Poor Comparative Example B15 569 608 13 10  13  58 93 5.8 0.010 Good Poor Comparative Example B16 551 1076  11 5 11  64 94 3.5 0.020 Good Poor Comparative Example B17 435 865  2 10  13  63 91 6.2 0.022 Good Poor Comparative Example B18 430 673  3 6 15  73 93 4.5 0.025 Good Poor Comparative Example B19 620 752 17 3 9 68 90 7.4 0.017 Good Poor Comparative Example B20 630 708 19 3 12  82 96 2.6 0.009 Good Poor Comparative Example B21 660 961 18 7 15  59 95 2.2 0.020 Good Poor Comparative Example B22 518 1021  18 2 12  78 94 4.1 0.020 Poor Poor Comparative Example B23 477 912 17   1.5 14  58 96 2.4 0.011 Poor Poor Comparative Example B24 536 809 20 1 14  88 92 5.8 0.020 Poor Poor Comparative Example B25 547 641 10 40  9 89 92 6.2 0.020 Good Poor Comparative Example B26 502 998  7 50  12  79 90 7.4 0.014 Good Poor Comparative Example B27 509 903  8 35  8 53 95 3.2 0.008 Good Poor Comparative Example B28 520 1047  11 10    0.5 57 94 4.3 0.025 Poor Poor Comparative Example B29 500 638 13 4   0.4 57 95 3.6 0.016 Poor Poor Comparative Example B30 511 757 13 7 40  61 95 2.7 0.007 Poor Poor Comparative Example B31 578 716 14 8 25  95 95 3.9 0.015 Poor Poor Comparative Example B32 496 699 11 4 30  63 91 6.3 0.013 Poor Poor Comparative Example B33 581 906  6 5 27  52 93 4.7 0.024 Poor Poor Comparative Example B34 535 1001  14 9 1 64 96 3.1 0.016 Poor Poor Comparative Example B35 543 882 11 5   0.4 93 97 1.3 0.011 Poor Poor Comparative Example B36 550 727  8 7 33  60 93 4.8 0.026 Poor Poor Comparative Example B37 477 830 12 7 1 65 96 2.4 0.017 Poor Poor Comparative Example B38 543 847  9 5   0.5 69 90 6.8 0.015 Poor Poor Comparative Example B39 526 695 10 5   0.5 76 90 7.3 0.015 Poor Poor Comparative Example Note: Underlined value is out of range of the present invention.

INDUSTRIAL APPLICABILITY

The alloyed hot-dip galvanized steel sheet manufactured using the method according to the present invention has a high strength with a tensile strength of 590 MPa or more, and has excellent wettability of plating and adhesion of plated layer. Accordingly, it is expected that the alloyed hot-dip galvanized steel sheet is applied as a material used in an automotive field, a household appliance field, and a building material field. 

1. A method of manufacturing an alloyed hot-dip galvanized steel sheet using a base steel material, the base steel material containing, in mass %, C: more than or equal to 0.05% and less than or equal to 0.50%, Si: more than or equal to 0.2% and less than or equal to 3.0%, Mn: more than or equal to 0.5% and less than or equal to 5.0%, Al: more than or equal to 0.001 and less than or equal to 1.0%, P: less than or equal to 0.1%, S: less than or equal to 0.01%, N: less than or equal to 0.01%, and the balance including Fe and inevitable impurities, the method comprising: performing casting, hot-rolling, pickling, and cold rolling to thereby produce the base steel material; subjecting the base steel material to a hot-dip galvanizing treatment by performing, using a continuous hot-dip galvanizing plant equipped with a heating furnace and a soaking furnace, an annealing treatment in which a temperature of the base steel material is increased within a range of higher than or equal to 500° C. and lower than or equal to 950° C. in the heating furnace and the soaking furnace; and subjecting the base steel material to an alloying treatment at higher than or equal to 440° C. and lower than or equal to 600° C., wherein the annealing treatment is performed under the following conditions: conditions of the heating furnace: an all radiant tube type heating furnace is used, a time period that the temperature of the base steel material is in the range of higher than or equal to 500° C. and lower than or equal to 950° C. is 100 seconds to 1000 seconds, an atmosphere of the heating furnace contains hydrogen, water vapor, and nitrogen, a logarithm log(P_(H2O)/P_(H2)) of a value obtained by dividing a partial water vapor pressure (P_(H2)o) by a partial hydrogen pressure (P_(H2)) is more than or equal to −4.0 and less than −2.0, and a hydrogen concentration is more than or equal to 3 vol % and less than or equal to 30 vol %; and conditions of the soaking furnace: a time period that the temperature of the base steel material is in the range of higher than or equal to 500° C. and lower than or equal to 950° C. is 100 seconds to 1000 seconds, an atmosphere of the soaking furnace contains hydrogen, water vapor, and nitrogen, a logarithm log(P_(H2O)/P_(H2)) of a value obtained by dividing a partial water vapor pressure (P_(H2O)) by a partial hydrogen pressure (P_(H2)) is more than or equal to −8.0 and less than −4.0, and a hydrogen concentration is more than or equal to 3 vol % and less than or equal to 30 vol %.
 2. A method of manufacturing the alloyed hot-dip galvanized steel sheet according to claim 1, wherein the base steel material further contains one or more of, in mass %, Cr: more than or equal to 0.05% and less than or equal to 1.0%, Ni: more than or equal to 0.05% and less than or equal to 1.0%, Cu: more than or equal to 0.05% and less than or equal to 1.0%, Nb: more than or equal to 0.005% and less than or equal to 0.3%, Ti: more than or equal to 0.005% and less than or equal to 0.3%, V: more than or equal to 0.005% and less than or equal to 0.5%, B: more than or equal to 0.0001% and less than or equal to 0.01%, Ca: more than or equal to 0.0005% and less than or equal to 0.04%, Mg: more than or equal to 0.0005% and less than or equal to 0.04%, La: more than or equal to 0.0005% and less than or equal to 0.04%, Ce: more than or equal to 0.0005% and less than or equal to 0.04%, and Y: more than or equal to 0.0005% and less than or equal to 0.04%. 